Custom built setups were developed to investigate micro samples during quasistatic and cyclic testing in tension, compression and bending. Micro molded CuAl10Ni5Fe4-samples showed similar fatigue behavior compared to macroscopic samples due to both the sample size and microstructure being scaled down with the manufacturing process. Results from cyclic three-point bending tests on micro molded 3Y-TZP suggested that a minimum crack extension is necessary to develop cyclically degradable shielding.